Surface morphology and phase stability effect of Ceria-Hafnia (CHx) binary metal oxides on soot oxidation activity

Anantharaman, Anjana P and Dasaria, Hari Prasad and Dasari, Harshini and Babu, Uday Bhaskar G (2018) Surface morphology and phase stability effect of Ceria-Hafnia (CHx) binary metal oxides on soot oxidation activity. Applied Catalysis A: General, 566 (1). pp. 181-189. ISSN 0926860X

[img] PDF
5029.pdf - Published Version
Restricted to Registered users only

Download (4MB) | Request a copy


CeO2-HfO2 (CHx) binary metal oxides over whole composition range (0–100%) are synthesised using the EDTACitrate method and calcined at 600 °C/5 h. From XRD analysis, the sample series are classified as fluorite (F) phase for CH10-CH30, hybrid (F+M) phase for CH40-CH90 and monoclinic (M) phase for CH100 sample, respectively and the results were further confirmed using Raman spectroscopy. From SEM analysis, a clear surface morphology change is noticed for fluorite, hybrid and monoclinic phases of the CHx binary metal oxides. Further, Selected Area Electron Diffraction (SAED) analysis also confirmed the single and hybrid phases of CHx binary metal oxides. The soot oxidation for the CHx binary metal oxides displayed high catalytic activity for Fluorite phase (CH10 ∼ CH30) samples and a decrease in catalytic activity is noticed for the Hybrid phase (CH40 ∼ CH90) samples. The change in catalytic activity coincides with the change in the surface morphology and phase change for the CHx binary metal oxides. Among the Fluorite phase samples, CH10 sample displayed the highest catalytic activity (T50=430 °C) with higher surface area (29 m2/g), lower particle size (26 nm), lower degree of agglomeration (ϕ=2.8) higher surface oxygen concentration (44%). Isothermal-Time-onstream (ITOS) analysis also showed that the CH10 sample can achieve T50 in a shorter time than compared to other CHx binary metal oxides. Surface morphology and phase stability can also play as key descriptors in screening CHx binary metal oxides for soot oxidation activity.

Item Type: Article
Uncontrolled Keywords: Ceria-Hafnia Secondary phase,Surface morphology, XRD analysis, Soot oxidation
Subjects: Engineering > MIT Manipal > Chemical
Depositing User: MIT Library
Date Deposited: 11 Sep 2018 04:55
Last Modified: 11 Sep 2018 04:55

Actions (login required)

View Item View Item