Comparative Evaluation of Tensile Bond Strength and Shear Bond Strength of Mineral Trioxide Aggregate with Composite Resin and Resin Modified Glass Ionomer

S, Radhakrishnan and Rao, Arathi and Shenoy, Ramya and *, Suprabha BS (2019) Comparative Evaluation of Tensile Bond Strength and Shear Bond Strength of Mineral Trioxide Aggregate with Composite Resin and Resin Modified Glass Ionomer. Indian Journal of Public Health Research and Development, 10 (7). pp. 156-161. ISSN 09760245

[img] PDF
Comparative Evaluation of Tensile Bond Strength and Shear.pdf - Published Version
Restricted to Registered users only

Download (527kB) | Request a copy

Abstract

Background:In a vital pulp therapy such as direct pulp capping or pulpotomy, MTA is directly placed over the pulp followed by the restoration with resin modified glass ionomer cement or composite material. An important factor determining the clinical success of such restorations is the bond between MTA and restorative material. Therefore, the aim of the present study was to evaluate and compare the bond strength of MTA with Glass Ionomer and Composite resin interface.Material and Method: The sample size was calculated as 11 in each group. Tensile and shear bond strength was measured between MTA- Glass Ionomer and MTA- Composite material. Percentage of bond failure for each group was obtained. Average and standard deviations were calculated and the data was analyzed by independent‘t’ test. The level of significance was set at 0.05.Results: Out of the total 44 samples, 29 samples showed cohesive failures. Maximum numbers of failures, i.e. 17 were in tensile bond strength group which included 8 in RMGIC group and 9 in Composite resin group. Of the 12 failures in shear bond strength, 5 were in RMGIC group and 7 in composite resin group. There was no statistically significant difference between the shear bond strength of RMGIC and Composite with MTA (p = 0.39) at confidence interval of 95%. No statistically significant difference was observed between the tensile bond strength of RMGIC and Composite samples with MTA (p = 0.41) at confidence interval of 95%.Conclusion: There was no difference in the bond strengths attained between Resin modified Glass ionomers and Resin Composites with Mineral trioxide Aggregate

Item Type: Article
Uncontrolled Keywords: Mineral Trioxide Aggregate, Glass Ionomer, Composite Resin, Bond strength
Subjects: Dentistry > MCODS Mangalore > Public Health Dentistry
Dentistry > MCODS Mangalore > Pedodontics
Depositing User: KMCMLR User
Date Deposited: 10 Aug 2019 03:39
Last Modified: 10 Aug 2019 03:39
URI: http://eprints.manipal.edu/id/eprint/154354

Actions (login required)

View Item View Item