Effect of Ag loading on praseodymium doped ceria catalyst for soot oxidation activity

Govardhana, Panduranga and Anantharaman, Anjana P and Patil, Sunaina Shivasharanappa and Dasari, Hariprasad and Dasari, Harshini and Shourya, Atmuri (2022) Effect of Ag loading on praseodymium doped ceria catalyst for soot oxidation activity. Korean Journal of Chemical Engineer. ISSN 0256-1115

[img] PDF
13899.pdf - Published Version
Restricted to Registered users only

Download (8MB) | Request a copy

Abstract

Silver-loaded praseodymium doped ceria (XAg/PDC) was synthesized by microwave-assisted co-precipita�tion and wetness impregnation. XRD confirms the fluorite structure of ceria without secondary phase, and Raman spectroscopy represents the increased generation of oxygen vacancies with Ag loading. The TEM analysis shows lattice fringes corresponding to both CeO2 and Ag on the surface. The BET and BJH analysis of catalyst confirms the high porosity accompanied by high surface area and pore diameter of 5Ag/PDC and 15Ag/PDC, making it more active for the oxidation reaction. From the XPS analysis the amount of surface Ce3+ concentration and the surface chemisorbed oxygen species (O2 2 ) is high for 5Ag/PDC and 15Ag/PDC, in line with XRD and Raman results. The soot oxidation T50 temperature follows the trend: 5Ag/PDC~15Ag/PDC>10Ag/PDC>20Ag/PDC>0Ag/PDC. The Ag loading increased the surface reducibility of cerium ions and thus 5 wt% was optimized

Item Type: Article
Uncontrolled Keywords: Praseodymium-doped Ceria (PDC), Ag Loading, Reducibility Microwave-assisted Co-precipitation, Oxygen Vacancies, Soot Oxidation Activity
Subjects: Engineering > MIT Manipal > Chemical
Depositing User: MIT Library
Date Deposited: 23 Mar 2022 09:23
Last Modified: 23 Mar 2022 09:23
URI: http://eprints.manipal.edu/id/eprint/158440

Actions (login required)

View Item View Item